The Analysis of Two-part Epoxy Adhesive
by ionRocket

 

 

Background

The hardening of two-part epoxy adhesive starts by mixing epoxy resin with a hardening accelerator. The analytical method of hardening materials is limited, because of the low amount of sample, and its difficulty to solubilize. The hardened material was analyzed with ionRocket heating system connected to the DART®-MS without pretreatment.

 

Method

The analyzing tool was the ionRocket heating system connected to the DART®-MS (Direct Analysis in Real Time – Mass Spectrometry).

 

Result

TIC is shown in Fig 1. MS spectra measured at 200ºC is shown in Fig 2.
In Fig 2, the principal component of solution A was BADGE (bisphenol A diglycidylether) and bisphenol A diacetate. The principal solution B was accelerating agent DMP-30.

Fig.1 TIC of each sample. R.T. 100°C/min 600°C
Fig. 2 MS spectrum measured at 200°C. The preset temperature of DART®-SVP was 400°C. Ionization was DART® positive.

 

 

Target

Adhesive Material Development /Chemical industry / Foreign Material Analysis

 